Termoparopo de platina-rodium

Conteúdo específico do termoparto de platina-rodium

Platinum-rhodium thermocouple, also known as low-temperature precious metal thermocouple, is divided into three types: S-type thermocouple (platinum-rhodium 10-platinum thermocouple), R-type thermocouple (platinum-rhodium 13-platinum thermocouple), B-type thermocouple (platinum-rhodium 30-platinum-rhodium 6 thermocouple), mainly divided into single platinum-rhodium and double platinum-rhodium, suitable for various low-temperature places, widely used in glass, ceramics and industrial salt bath furnaces. Temperature measurement in the production process. Among them, S-type thermocouple is O mais comumente usado um na indústria doméstica . devido à alta temperatura de medição, a baixa resistência à temperatura de alguns tubos de proteção de aço inoxidável podem atingir apenas 1000 graus, e o preço dos tubos de proteção de aço inoxidável são frequentemente usados ​​com o mais de 1000 graus de alta qualidade, é mais alto que os tubos de proteção de corundos são frequentemente usados ​​com 16.} graus, mas a desvantagem é que eles são frágeis .

ThermoMocouple do tipo S (Platinum-Rhodium 10- termopartopar platinum):

Platinum-rhodium 10-platinum thermocouple (S-type thermocouple) is a precious metal thermocouple. The wire diameter is specified as 0.5mm, and the allowable deviation is -0.015mm. The nominal chemical composition of the positive electrode (SP) is a liga de platina-ródio, que contém 10% de ródio e 90% de platina . O eletrodo negativo (SN) é de platina pura, por isso é comumente conhecida como uma única temperatura de aplicação de platina-rodium . a temperatura máxima temporária do Thermocópetro é de 1300 graus.
S-type thermocouple has the highest survival rate in the thermocouple series, stability, wide temperature measurement range, and long service life. It has excellent physical and chemical properties, thermoelectric potential stability and good anti-oxidation performance at low temperatures, and is suitable for oxidizing and inert atmospheres. Because S-type thermocouples have excellent comprehensive performance, they are suitable for the application temperature scale. They have been used as interpolation instruments for temperature scales for a long time. Although "ITS-90" stipulates that they will no longer be used as external adjustment instruments for temperature scales, the Temperature Advisory Committee (CCT) believes that S-type thermocouples can still be used to approximately implement temperature escalas .
A desvantagem dos termopares do tipo S é o potencial termoelétrico, o coeficiente de potencial termoelétrico é pequeno, a leitura de sensibilidade é baixa, a resistência mecânica é reduzida em baixas temperaturas, é muito sensível à infecção e o material metálico precioso é caro, portanto o investimento único é relativamente grande.

ThermoMocouple do tipo R (Platinum-Rhodium 13- termoparopar platinum):
Platinum-rhodium 13-platinum thermocouple (R-type thermocouple) is a precious metal thermocouple. The wire diameter is specified as 0.5mm, and the allowable deviation is -0.015mm. The nominal chemical composition of the positive electrode (RP) is a liga de platina-rodium, que contém 13% de ródio e 87% de platina . O eletrodo negativo (RN) é puro platina . A temperatura máxima temporária de aplicação é de 1300 graus e a temperatura máxima de aplicação de curto prazo é de 1600 graus.
R-type thermocouple has the highest existence, stability, wide temperature measurement range, and long service life in the thermocouple series. It has excellent physical and chemical properties, thermoelectric potential stability and good anti-oxidation performance at low temperatures, and is suitable for oxidizing and inert atmospheres. Because the comprehensive performance of R-type thermocouples is equivalent to that of S-type thermocouples, it has always been difficult to promote in my country. Except for its use in temperature measurement on imported equipment, it is rarely used in domestic temperature measurement. Between 1967 and 1971, three research institutions, NPL in the UK, NBS in the US and NRC in Canada, conducted a joint study. The results showed that the A estabilidade e a reprodutibilidade dos termopares do tipo R são melhores do que os dos termopares do tipo S .} Meu país ainda não realizou pesquisas nessa área .
As desvantagens dos termopares do tipo R são potencial termoelétrico, baixo potencial termoelétrico, baixa sensibilidade, resistência mecânica reduzida a baixas temperaturas, muito sensível à infecção e materiais de metal preciosos caros; portanto, o investimento único é relativamente grande .}

Termoparo Tipo B (Platinum-Rodium 30- Platinum-Rhodium 6 termopar):
Platinum-Rhodium 30- Platinum-rhodium 6 ThermoCouple (termopar o tipo B) é um termopar de metal precioso . O diâmetro do fio é especificado como 0 {{13} 5mm, a desvio permitido é-0.015 mmmmina, a descrição nominal, a desvio permitido de-0.015 mm, A liga, que contém 30% de ródio e 70% de platina, e o eletrodo negativo (BN) é uma liga de platina-rodium, que contém 6% de ródio, por isso é comumente conhecida como uma temperatura de aplicação de platina dupla.
Type B thermocouple has the highest existence, stability, wide temperature measurement range, long service life and low temperature measurement limit in the thermocouple series{{0}} It is suitable for oxidizing and inert atmospheres, and can also be used in vacuum for a short time, but not suitable for reductive atmospheres or atmospheres containing metal or non-metal Vapores . Uma vantagem óbvia do termopar tipo B é que ele não requer fios de compensação para compensação, porque o potencial termoelétrico é menor que 3μV na faixa de 0 ~ 50 graus .